MULTIPLE CRACKS LOCALIZATION FOR THIN COATING FILM LAYERS IN PURE BENDING

2018

Recently, accurate small scale four-point bending flexural tests, for superalloy specimens with multiple ceramic type external coating film layers, have shown that under high loading, the failure mechanism is characterized by the development of complex multiple surface cracks, followed by interior interlayers debonding mechanisms. The final stage is then the complete debonding of the fragmented thermal coating, which leave the interior superalloy completely uncoated. The mechanical problem has an high technological relevance, since failure, or just severe damage, of the ceramic coating, can jeopardize the functionality of structural elements working at high temperature and under severe load…